Phase Formation and Diamond Retention in Cdiamond–(WC–Co)–ZrO2 Composites Formed by Spark Plasma Sintering Method

2024

Closed access Metadata (CSL-JSON)
DOI 10.3103/s1063457624020084
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

Abstract New data on the effect of a ZrO2 nanopowder additive (from 0 to 10 wt %) on phase formation and structural transformations in the hard-alloy matrix in the region of destruction under impact loading and on diamond retention in composite diamond-containing 25Сdiamond–70.5WC–4.5Co materials formed by spark plasma sintering are presented. The sintered initial 94WC–6Co composite consists of the hexagonal WC phase with unit cell parameters a = 0.2906 nm and с = 0.2837 nm, the cubic Co3W3C phase (а = 1.1112 nm), and the hexagonal graphite phase. The sintered composites with ZrO2 content from 0.5 to 10% is composed by the WC and Co3W3C structural phases, amorphous carbon, and the tetragonal ZrO2 phase (а = 0.36019 nm, с = 0.5174 nm). It has been shown that, when the ZrO2 content is increased, the sizes of phase components and average microstrains are more rapidly decreased in directions с and а of the 94WC–6Co composite. The addition of ZrO2 to the 25Сdiamond–70.5WC–4.5Co composite improves diamond retention. In the sintered composites, diamond retention is improved due to that they have a higher content of the tetragonal ZrO2 phase, which provides the transformational mechanism of strengthening in the hard-alloy matrix material via its structural transformations into a denser one and the formation of a more fine-grained matrix structure with thin interlayers of cobalt bonds between WC grains.