Synthesis and microwave absorption properties of Ni0.5Zn0.5Fe2O4/CI composite coated with polyaniline within paraffin wax matrix

anas houbi, Zharmenov Aldashevich, Yomen Atassi, Zhenisgul Telmanovna, MIRZALIEVA Saule

2022

Full text Open access: Green Metadata (CSL-JSON)
DOI 10.21203/rs.3.rs-1637416/v1
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

Abstract In this paper, Ternary composites of polyaniline/NiZn ferrite/carbonyl iron (PANI/F/CI) are prepared via two stages: Firstly, Ni0.5Zn0.5Fe2O4 is prepared using a sol-gel method while carbonyl iron is commercially purchased. After that, PANI/F/CI composites are prepared using an in-situ polymerization technique of PANI in the existence of the Ni0.5Zn0.5Fe2O4 and CI. X-ray diffractometry, FTIR spectroscopy, UV-vis spectroscopy, TGA analysis, and SEM analysis are utilized in order to characterize samples. The morphology of the powders is investigated by SEM. The electromagnetic interference shielding and microwave absorption properties are measured in the frequency band of 8.8–12 GHz to investigate the microwave characterization. The results refer those microwave absorption properties are related to the absorber thickness and the loading ratio of the absorber within a paraffin matrix. Minimal reflection loss of -30.8 dB at the matching frequency of 10.3 GHz and the absorption bandwidth under − 10 dB of 2.8 GHz for 3.4 mm thickness with a surface density of 3.38 kg/m2 are noticed for the PANI/F/CI composite sample. The maximum shielding efficiency of 30.12 dB at 11.0 GHz for 3.2 mm thickness is observed for the PANI/F/CI composite sample.