Obtaining multilayer coatings by the detonation spraying method

Dauir Kakimzhanov, Bauyrzhan K. Rakhadilov, Dastan Buitkenov, Laila Gylymmeddenovna Zhurerova, Merey Rakhadilov, Didar Yeskermessov

2021

Data confidence 70 medium

How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

This work were studied the effect of technological parameters of detonation spraying on the phase composition and tribological characteristics on the bases of NiCr and Al2O3 coatings. As well as there was obtained and investigated multilayer coating on the bases of NiCr/NiCr- Al2O3/Al2O3 . It was determined that during detonation spraying the phase composition of Al2O3 coatings strongly depends on the degree of filling the borehole with a gas mixture. The a - Al2O3 -phase content in the coatings increases when the degree of filling is 63% and 54%. Only one CrNi3 phase is observed on the diffractograms and only increase of reflex intensity (020) at barrel filling by 58% is observed by sputtering on the bases of NiCr coatings in different degrees of barrel filling. The results of the coating nanohardness study showed that the hardness of the Al2O3 coating increases depending on the content of a- Al2O3 in it. Al2O3 coating has the maximum nanohardness values and is 16.42 GPa at the borehole is filled to 63%. The nanohardness of NiCr coating has the maximum values at barrel filling by 58% and consisting of 8.02 GPa.