Influence of electrolytic-plasma hardening modes on structure and hardness of 0.34Cr-1Ni-Mo-Fe steel

Bauyrzhan K. Rakhadilov, Zarina A. Satbayeva, Rauan S. Kozhanova, Daryn Baizhan, Merey Rakhadilov, G. B. Botabaeva

2020

Full text Open access: Gold Metadata (CSL-JSON)
DOI 10.29317/ejpfm.2020040406
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

The article presents the results of studying the process of electrolytic-plasma hardening of 0.34Cr-1Ni-Mo-Fe steel by surface hardening, as well as the results of the current-voltage characteristics of the cathodic electrolytic-plasma process depending on the composition of the electrolyte. Temperature-time and special modes of electrolytic-plasma hardening of steel 0.34Cr-1Ni-Mo-Fe were determined. The optimal composition of the electrolyte for electrolytic-plasma hardening has been determined, providing a relatively high heating rate and high hardness of the steel surface. It has been determined that after the electrolytic-plasma hardening, the microhardness of 34KhN1M steel increases 2.9 times due to the formation of fine martensite. In this case, the basis of the material does not change, it consists of a ferrite-pearlite structure.