Abstract
Wear of the working surfaces of machinery parts is a phenomenon that cannot be fully countered, only postponed. Among surface lifecycle elongation techniques, hardfacing is one which is most often used in heavy load applications. Hardfaced coating can be applied using different welding approaches or thermal spraying technologies, which differ when it comes to weld bead dimensional precision, layer thickness, process efficiency and material. In this study the authors examine the geometrical behavior and hardness properties of two distinctive chromium-based Gas Metal Arc Welding (GMAW) cored wires. The stringer beads are applied numerically with five levels of linear energy, being a resultant of typical values of welding speed and wire feed, ranging between 250 mm/s to 1250 mm/s (welding speed) and 2 m/min to 10 m/min (wire feed). The samples were cut, etched and measured using a digital microscope and Vickers indenter, additionally the chemical composition was also examined. Hardness was measured at five points in each cutout, giving 40 measurements per sample. The values were analyzed using an ANOVA test as a statistical background in order to emphasize the divergent behavior of the cored wires. It appeared that, despite having less chromium in its chemical composition, wire DO*351 exhibits higher hardness values; however, DO*332 tends to have a more stable geometry across all of the heat input levels.