Synthesis of Core/Shell ZnO/rGO Nanoparticles by Calcination of ZIF-8/rGO Composites and Their Photocatalytic Activity

Batukhan Tatykayev, Florian Donat, Halima Alem, Lavinia Balan, Ghouti Medjahdi, Bolat Uralbekov, Raphaël Schneider

ACS Omega, 2017

Full text Open access: Gold Metadata (CSL-JSON)
DOI 10.1021/acsomega.7b00673
Data confidence 85 high
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

Abstract A facile two-step method was developed to prepare core/shell ZnO/rGO particles from ZIF-8/rGO composites. ZIF-8 particles were first grown at the surface of rGO sheets. Next, ZIF-8 particles were transformed into ZnO particles by thermal decomposition under air at 500 °C. All materials were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, Raman spectroscopy, thermogravimetric analysis, and Brunauer–Emmett–Teller analyses. Results obtained show that ZIF-8 particles strongly associate with rGO sheets and that the calcination of this material produces porous core/shell ZnO/rGO particles with an average diameter of ca. 40 nm. The wt % of rGO associated with ZIF-8 particles was varied from 5 to 20%. The ZnO/rGO (10%) particles exhibit the highest photocatalytic activity for the degradation of the Orange II dye under simulated solar light irradiation of weak intensity (5 mW/cm2). This high photocatalytic activity was demonstrated to originate from superoxide O2•– radicals due to the efficient trapping of photogenerated electrons in ZnO by rGO.