Abstract
Electron microscopy and x-ray analysis and mechanical testing have been investigated the influence of severe plastic deformation on structure and mechanical properties of aluminum alloys. It is established that in the initial state in the alloy AMC has a high density of chaotically distributed dislocations with a density of 5-10*109 сm-2. It is shown that microdiffraction paintings in alloy AMC in the bulk of grains are observed uniformly distributed particles of the second phase. It is established that in the initial state in the alloy AMG6 there is a high density of chaotically distributed dislocations with a density of 2-6 *1010 сm-2. Determined that after ECAP the dislocation structure of alloys AMG6, AMC and changes: formed dislocation networks inside the fragments of the dislocation is practically not observed. Determined that after ECAP-12 increase the tensile strength and yield strength of alloys AMG6 and AMC.