γ→α’ Martensitic Transformation in the Reactor Steels Under Irradiation and Deformation

2014

Full text Open access: Gold Metadata (CSL-JSON)
DOI 10.5755/j01.ms.20.1.1904
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

Complex studies of the 12Cr18Ni10Ti and Cr15Mn14 reactor steels in the initial, deformed states, and after irradiation with the and WC+ heavy ions were conducted. Peculiarities of the α’-martensite phase content and mechanical characteristics of the specimens, which were deformed after the irradiation were examined. It was shown that the martensite phase existed in the irradiated and deformed specimen at two scale levels. Electron Backscattered Diffraction (EBSD) revealed that the difference between the unirradiated and irradiated specimens was the formation of the α’-martensite and ε-martensite in the near surface layer of the irradiated specimen. It was determined that the fluence value has affect on the α’-magnetic phase. Thus, chrome-nickel steels of 12Cr18Ni10Ti type show better resistance to irradiation with the heavy WC+ ions in comparison with manganese steel of Cr15Mn14 type, as less martensite of irradiation forms in them.DOI: http://dx.doi.org/10.5755/j01.ms.20.1.1904