Structure and Properties of SiC Coated R6M5 High-Speed Steel

Маzhyn Skakov, Bauyrzhan K. Rakhadilov, Gaukhar Karipbayeva

2013

Full text Open access: Hybrid Metadata (CSL-JSON)

DOI 10.4028/www.scientific.net/kem.594-595.730

Data confidence 70 medium

How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

A Possibility of R6M5 High-Speed Steel Strengthening by Finishing Plasma Strengthening(FPS) Method to Application of Sic Thin Film Coatings were under Research. by Scanning Electronmicroscopy and X-Ray Analysis Conducted a Comparative Study of the Structure, Phase and Chemicalcomposition before and after Application of Sic Thin Film Coating of R6M5 High-Speed Steel Surfacelayer. it is Experimentally Stated, that the Coverage of Sic Applied Method FPS Consists of Fineglobular Shape at the Size of 100-300 Nm. Determined that the Microhardness of R6M5 Steel Surfaceafter Application Sic Coating Increased Almost to 2.5 Times Comparing to Original. it is Shown Thatthe Application of Sic Thin Film Coating by FPS Method is a Promising Highly Effective Method Ofcutting Tools Surface Strengthening Made from High Speed Steels.