Abstract
Due to the widespread use of microwave electromagnetic radiation, this study examines the microwave electromagnetic properties and compressive strength of composites made from inexpensive components such as Mg0.5Zn0.5Fe2O4, polystyrene, and activated carbon. Experimental samples were fabricated using thermopressing. The formation of the dielectric core/shell structure for Mg-Zn/polystyrene composites (1:1) and composites with activated carbon additives at weight concentrations of 3, 6.6, and 9.0% was determined using SEM image analysis. Microwave properties were investigated by analyzing the frequency dependences of complex permittivity and magnetic permeability in the frequency range of 100 MHz–5 GHz. As shown by the simulation and experimental measurements of scattering parameters obtained, the compost shows improved microwave absorption properties in the frequency range of 1–5 GHz. Reflection loss spectra showed peaks with values of −17.8 and −18 dB in the frequency range of 2.5–5 GHz for samples with 4.8 wt. % and 6.6 wt. % carbon loading, respectively. The absorption bandwidths of −10 dB in the range of 1.7–2.13 GHz were observed in the best samples. Studies have shown that samples containing 9.0 wt. % of carbon material with thicknesses of 6–10 mm can be considered as an electromagnetic shielding material in the microwave range 1–5 GHz. It was shown that, despite a decrease in porosity from 15.59 to 7.17%, with an increase in the concentration of carbon material in the composites, the compressive strength also decreases from 62.05 to 36.45 MPa. The developed composites are potentially suitable as microwave absorbers for civil applications.