Abstract
Carbon-enriched concentrates based on shungite ore from rare-metal mining waste were obtained, and their effect on the properties of oil- and fuel-resistant carbon-black-filled rubber used for the production of pressure hoses was investigated. The shungite concentrates were produced by flotation followed by acid activation. A blend of nitrile butadiene rubber and butadiene-α-methylstyrene rubber was used as the elastomeric base. Carbon black was partially replaced with shungite fillers (5-15 phr). The presence of shungite was found to prolong both the scorch time and the optimum cure time of the rubber compounds, likely due to oxide impurities that interfere with the vulcanization activation process. Replacing carbon black with shungite ore and its flotation concentrate in the rubber formulations resulted in a decrease in Mooney viscosity compared to the samples without shungite fillers. Acid-activated shungite concentrate at contents above 5 phr increases the viscosity of the rubber compound. It was found that acid-activated shungite concentrate provides high tensile strength and excellent thermo-oxidative stability of the rubber, whereas the use of shungite ore above 5 phr reduces the tensile strength and causes significant changes in tensile properties upon thermo-oxidation. When exposed in oil, rubbers containing shungite fillers retain their mechanical properties, with the best resistance in hydrocarbon media observed for the rubber filled with acid-activated shungite concentrate.