Electrical and dielectric properties of rare earth substituted hard-soft ferrite (Co0.5Ni0.5Ga0.01Gd0.01Fe1.98O4)x/(ZnFe2O4)y nanocomposites

Munirah Abdullah Almessiere, Bayram Unal, A. Demir Korkmaz, Sagar E. Shirsath, Abdulhadi BAYKAL, Y. Slimani, M.A. Gondal, Umair Baig, Alex V. Trukhanov

Journal of Materials Research and Technology, 2021

Full text Open access: Gold Metadata (CSL-JSON)
DOI 10.1016/j.jmrt.2021.08.049
Data confidence 85 high
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

ZnFe2O4 (ZFO) NPs (nanoparticles), Co0.5Ni0.5Ga0.01Gd0.01Fe1.98O4 (CNGaGdFO) NPs and hard-soft spinel ferrite (H/S) (CNGaGdFO)x/(ZFO)y (x:y = 1:1, 1:2, 1:3, 2:1, 3:1 and 4:1) NCs (nanocomposites) were synthesized via a one-pot sol–gel auto combustion route. X-ray powder diffraction (XRD) analyses confirmed the purity of ZFO NPs, CNGaGdFO NPs and H/S (H/S) (CNGaGdFO)x/(ZFO)y (x:y = 1:1, 1:2, 1:3, 2:1, 3:1 and 4:1) (absence of any second phase). The crystallite size of NCs was between 39 and 52 nm. The cubic morphology was observed for ZFO NPs, CNGaGdFO NPs and all H/S NCs by the help of scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analyses. Energy dispersive X-Ray analysis (EDX) also confirmed the chemical formula of all the NC samples. Electrical and dielectric properties of ZFO NPs, CNGaGdFO NPs and H/S NCs were explored with an impedance analyzer with f ≤ 3.0 MHz, where f stands for frequency, and within the temperature range between 20 and 120 °C. Electric and dielectric parameters such as AC conductivity as well as DC conductivity, activation energy, dielectric constant, dielectric loss in addition to the dissipation parameter relevant to the electrical energy due to different physical processes were measured for each of the given compositional ratios. The AC conductivity was found to follow the frequency-dependent power law in general, being mainly reliant on the compositional ratios and the measured temperatures especially at lower frequencies. This study has shown that CoNiGaGdFeO-ZnFe2O4 H/S NCs carry out conduction mechanisms, which can be predominantly credited to grain–grain boundaries for various compositional ratios. The dielectric constant of (CNGaGdFO)x/(ZFO)y (x:y = 1:1, 1:2, 1:3, 2:1, 3:1 and 4:1) H/S NCs indicates common dielectric behaviours with frequency, largely dependent on compositional rates of the hard to soft spinel ferrites. It is observed that hard ferrite is dominant in the formation of the semicircles, and the diameter of the semicircles shows a drop as the temperature rises, suggesting a temperature-dependent relaxation mechanism. Consequently, the observed variation of the studied dielectric parameters with frequency can be explained by the conduction mechanism in most composition ratios of hard to soft spinel ferrites, which can be explained by a phenomenological method with Koop's model.