X-ray diffraction analysis of reorientation regions formed in [111]-single crystal of aluminum under compression

Беспалова Ирина Валерьевна, Ludmila A. Teplyakova

2015

Full text Open access: Gold Metadata (CSL-JSON)

DOI 10.1088/1757-899x/71/1/012058

Data confidence 70 medium

How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

The paper presents results of the crystalogeometric analysis of the shear pattern formed on lateral faces of a single crystal of aluminum under compression along the direction [ 11] . Main features of shear strain in [ 11] -single crystals of aluminum have been revealed. Typical elements of strain relief have been identified and places of their location have been established. Occurrence of a bending in the crystal lattice at the macro level has been established using the Laue pattern method. The results of the X-ray analysis have been compared with the shear pattern.