The effect of methyldiethanolamine (MDEA) aqueous solution ageing on the corrosion mechanisms of A414(F) steel under acidic conditions

Arlan Z. Abilmagzhanov, Nikolay S. Ivanov, I.Y. Adelbayev, Nataliya A. Ivanova, Sergey K. Oparin, Oleg S. Kholkin, Vladislav V. Kudryashov

Results in Engineering, 2026

Full text Open access: Gold Metadata (CSL-JSON)
DOI 10.1016/j.rineng.2026.108968
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

• The corrosion morphology of A414(F) steel depends on the MDEA solution composition • The corrosion behavior of A414(F) in Fresh vs Aged MDEA solution was tested • The extreme corrosion rate is driven by the local H 2 SO 4 impact and Cl-ions presence • A protective FeS 2 film grows in the presence of H 2 S, which prevents corrosion The comprehensive analysis of the A414(F) structural steel corrosion mechanism in an aqueous methyldiethanolamine (MDEA) solution degraded under real industrial conditions (Aged) vs Fresh one was conducted. The accelerated corrosion test was conducted at 150°C to evaluate the corrosion activity of the solutions. The relationship between the composition of the aged solution and the steel corrosion morphology was examined. The results showed that A414(F) steel corroded at a low rate of about 0.16 mm/year in the Fresh MDEA solution. However, the corrosion rate increased extremely up to 9.2 mm/year (∼ 60 times higher) when the coupons were tested in the Aged MDEA solution. This was attributed to a complex corrosion mechanism involving the destruction of the protective oxide film in the presence of chloride ions, as well as to the local H 2 SO 4 -acid corrosion in the presence of elemental sulfur due to mercaptans (precursors to elemental sulfur). Saturation of the Aged MDEA solution with hydrogen sulfide has a strong inhibitory effect (∼93% of the inhibition efficiency), reducing the corrosion rate of steel from 9.2 mm/year to 0.62 mm/year, a reduction of more than 15 times. This finding underscores protective properties of a dense FeS 2 -pyrite film, even in the presence of other aggressive agents, which has practical implications for industrial corrosion control. Based on the data obtained, direct recommendations were provided for improving corrosion management in industry.