Abstract
This work presents the results of the study on the effect of pulse-plasma treatment on the structural-phase states of the surface layer of detonation coatings based on Ti3SiC2. Structural-phase studies were carried out by three main methods: scanning electron microscopy, transmission electron diffraction microscopy on thin foils and X-ray structural analysis. It was determined that after the pulse-plasma treatment, an increase in the intensity of the Ti3SiC2 peaks was observed, and the appearance of new reflections (101, 102, 112, 204, 1110, 0016) of this phase was detected, which indicates the increase in the MAX-phase content. It was determined that after the pulse-plasma treatment, the fraction of voids (pores) and the particle area decreased and the microstructure became more homogeneous, which resulted in the densification of the Ti3SiC2-based detonation coating. It was found that the process of detonation spraying with subsequent pulse-plasma treatment resulted in the formation of a Ti3SiC2-based coating, with TSC carbosilicide (Ti3SiC2) 0] plane reflexes, lamellar layered structure, and reduced porosity.