High-Energy Heavy Ion Tracks in Nanocrystalline Silicon Nitride

A. Janse van Vuuren, Alisher Mutali, Anel D. Ibrayeva, Alexander S. Sohatsky, Vladimir A. Skuratov, Abdirash T. Akilbekov, Alma K. Dauletbekova, Maxim Vladimirovich Zdorovets

Crystals, 2022

Full text Open access: Gold Metadata (CSL-JSON)

DOI 10.3390/cryst12101410

Data confidence 85 high

How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

At present, silicon nitride is the only nitride ceramic in which latent ion tracks resulting from swift heavy ion irradiation have been observed. Data related to the effects of SHIs on the nanocrystalline form of Si3N4 are sparse. The size of grains is known to play a role in the formation of latent ion tracks and other defects that result from SHI irradiation. In this investigation, the effects of irradiation with high-energy heavy ions on nanocrystalline silicon nitride is studied, using transmission electron microscopy techniques. The results suggest that threshold electronic stopping power, Set, lies within the range 12.3 ± 0.8 keV/nm to 15.2 ± 1.0 keV/nm, based on measurements of track radii. We compared the results to findings for polycrystalline Si3N4 irradiated under similar conditions. Our findings suggest that the radiation stability of silicon nitride is independent of grain size.