Solidification of the eutectic Ga–Sn alloy

В. Д. Александров, S. A. Frolova, Амерханова Шамшия Кенжегазиновна

2016

Closed access Metadata (CSL-JSON)
DOI 10.1134/s0036029516050025
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

Cyclic thermal analysis is used to study the effect of overheating of the eutectic Ga–8.5 mol % Sn melt on the presolidification supercooling. It is found that, when the liquid eutectic is overheated above the eutectic temperature (T e = 293.5 K) and is subsequently cooled, the dependence of the presolidification supercooling on the overheating temperature exhibits monotonic ascending behavior. The maximum supercooling after heating of the melt to 339 K is 26 K. The kinetic and thermodynamic parameters of eutectic solidification are calculated using the thermal analysis curves measured during melting.