Abstract
The article investigates the changing in the structure and phase composition of the R6M5 high-speed steel surface layer after electrolytic-plasma nitriding. It is found that after electrolytic-plasma nitriding on the R6M5 steel surface, modified layer is formed, which consist from a diffusion layer. It was showed phase composition of difysion layer is changing depending on the nitriding. It is found that electrolytic-plasma nitriding lead to accelerated formation of the modified layer. It is determined that after electrolytic-plasma nitriding on the high-speed steel surface, modified layer is formed, consisting only of the diffusion layer.