Salt tolerant acrylamide-based quenched polyampholytes for polymer flooding

Nurbatyr Mukhametgazy, Iskander Sh. Gussenov, Alexey V. Shakhvorostov, Sarkyt E. Kudaibergenov

2020

Closed access Metadata (CSL-JSON)
DOI 10.31489/2020ch4/119-127
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

In our previous papers [1, 2] we considered the behavior of linear and crosslinked polyampholytes based on fully charged anionic monomer — 2-acrylamido-2-methyl-1-propanesulfonic acid sodium salt (AMPS) and cationic monomer — (3-acrylamidopropyl)trimethylammonium chloride (APTAC) in aqueous-salt solutions, swelling and mechanical properties. In the present paper we report the applicability of salt tolerant amphoter-ic terpolymers composed of AMPS, APTAC and acrylamide (AAm) in enhanced oil recovery (EOR). The amphoteric terpolymers of different compositions, particularly [AAm]:[AMPS]:[APTAC] = 50:25:25; 60:20:20; 70:15:15; 80:10:10 and 90:5:5 mol.% were prepared by free-radical polymerization, identified and their viscosifying ability with respect to reservoir saline water (salinity is 163 g⋅L-1) at 60 °C was tested. It was found that due to polyampholytic nature, the AAm-AMPS-APTAC terpolymers exhibited improved viscosifying behavior at high salinity water. As a result, the appropriate salt tolerant sample [AAm]:[AMPS]:[APTAC] = 80:10:10 mol.% was selected for polymer flooding experiments. Polymer flood-ing experiments on high permeable sand pack model demonstrated that only 0.5 % oil was recovered by am-photeric terpolymer. While injection of polyampholyte solution into preliminarily water flooded core sample resulted in the increase of oil recovery up to 4.8–5 %. These results show that under certain conditions the amphoteric terpolymers have a decent oil displacement ability.