Optimization of Hydrochemical Leaching Process of Kaolinite Fraction of Bauxite with Response Surface Methodology

Yerkezhan Abikak, Arina Bakhshyan, Symbat Dyussenova, Sergey V. Gladyshev, Asiya Kassymzhanova

2024

Full text Open access: Gold Metadata (CSL-JSON)
DOI 10.3390/pr12071440
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

A technology for the hydrochemical processing of the kaolinite fraction of bauxite has been developed, and it involves preliminary chemical activation in a sodium bicarbonate solution and alkaline leaching in a recycled high-modulus solution with the addition of an active form of calcium oxide. Chemical activation allows for the transformation of the difficult-to-explore kaolinite phase to form easily soluble phases of dawsonite, sodium hydroaluminosilicate and bemite. An active, finely dispersed form of calcium oxide was obtained as a result of CaO quenching in Na2SO4 solution at elevated temperature and pressure. Using a central composite design (CCD) via response surface methodology (RSM), the technological leaching mode was achieved. The influence on the leaching process was studied by adjusting the CaO/SiO2 ratio, temperature, alkaline solution concentration and duration. It was found that the determining factors are the concentration of the leaching solution and the temperature. At a stable CaO/SiO2 ratio, a combination of these two factors determines the duration of the process to achieve the predicted degree of recovery. The results of experiments carried out using the developed model of the leaching process confirmed the validity of the calculated indicators, with an error of 2.01%. In an optimal technological mode at a Na2O leaching solution concentration of 260 g/L, a temperature of 260 °C, a CaO/SiO2 ratio of 1.5 and a leaching time of 5 h, the extraction of Al2O3 into the solution was 89.7%, which is close to the value of 87.9% predicted by the model.