Effect of Heat Treatment on Selective Laser Melted Ti6Al4V Alloys by adding Ta: Microstructure & Mechanical Properties

Anel Zhumabekova, Andrei Yankin, Asma Perveen

2026

Full text Open access: Hybrid Metadata (CSL-JSON)
DOI 10.1016/j.mfglet.2026.07.093
Data confidence 70 medium
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

This study investigates the effect of heat treatment on the microstructure and mechanical properties of (Ti6Al4V) 92 Ta 8 alloys produced by Selective Laser Melting. This research is motivated by the limited understanding of how β-stabilizing elements such as tantalum (Ta) influence phase evolution and mechanical performance in additively manufactured titanium alloys. The samples were subjected to heat treatment to compare as-built and heat-treated conditions. Microstructural characterization was performed using scanning electron microscopy to examine morphological changes, phase development, and Ta distribution. Mechanical testing included hardness measurements, tensile tests, and fatigue strength evaluations to assess variations in material response. After heat treatment, the alloy exhibited increased hardness and ductility, accompanied by higher strain and elastic modulus. However, ultimate tensile strength, yield strength, and fatigue strength decreased. These results indicate a transition toward more ductile behavior caused by microstructural coarsening and phase redistribution. Unmelted Ta particles persisted within the Ti6Al4V matrix due to the limited melting capability of SLM, while annealing promoted localized diffusion and grain reorientation around these regions. Overall, this study provides insight into the interaction between alloy composition, thermal treatment, and mechanical properties, highlighting the importance of optimizing heat treatment conditions to achieve a balanced combination of strength, ductility, and structural stability in SLM-produced titanium alloys.