Crack-Free and Thickness-Controllable Deposition of TiO2–rGO Thin Films for Solar Harnessing Devices

Laura Khamkhash, Svetlana Em, Anara Molkenova, Yoon‐Hwae Hwang, Timur Sh. Atabaev

2022

Full text Open access: Gold Metadata (CSL-JSON)

DOI 10.3390/coatings12020218

Data confidence 70 medium

How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

The use of thin films consisting of TiO2 and reduced graphene oxide (TiO2–rGO) in solar harnessing devices is gaining momentum thanks to improved charge-transporting characteristics. In this report, we propose a facile spin-coating methodology for the deposition of crack-free and thickness-controllable TiO2–rGO thin films. A range of characterization techniques were utilized to confirm the formation of the TiO2–rGO thin film. Improved charge-transporting properties of TiO2–rGO composite thin films were confirmed by measuring their photoelectrochemical (PEC) activity under simulated solar light illumination. In particular, it was found that the TiO2–rGO composite thin film yielded a better photocurrent response (~151.3 µA/cm2) than the bare TiO2 thin film (~71.6 µA/cm2) at 1.23 eV vs. the reversible hydrogen electrode (RHE). The obtained results suggested that rGO addition remarkably improves the charge-transporting properties in TiO2 films.