Structural and Phase State and Mechanical Properties of PEO Coatings on Al–Si Alloys with Al2O3 and SiO2 Nanoparticles

Kuat Kombayev, Gulzhaz Moldabayeva, Yernat A. Kozhakhmetov, Gulzhaz Uazyrkhanova, Yerkezhan Tabiyeva, Dauir Kakimzhanov

Bulletin of the Karaganda University Physics Series, 2026

Full text Open access: Gold Metadata (CSL-JSON)
DOI 10.31489/2026ph2/13-26
Data confidence 85 high
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

This paper presents the results of a comprehensive investigation of the structural, phase, and mechanical properties of plasma electrolytic oxidation (PEO) coatings formed on the surface of EN AC-45000 (AlSi6Cu4) aluminium–silicon alloy in an electrolyte containing Al2O3 and SiO2 nanoparticles. The aim of the study was to determine the effect of electrolyte nanomodification on the morphology, phase composition, and microhardness of PEO coatings. The PEO process was carried out in a NaOH-based aqueous electrolyte with the addition of aluminium and silicon oxide nanoparticles. The microstructure and morphology of the coatings were investigated using optical and scanning electron microscopy. The elemental and phase compo sition was determined by energy-dispersive analysis and X-ray diffraction. The mechanical properties were evaluated by measuring the microhardness using the Vickers method, while the tribological performance was assessed using the ball-on-disk method under dry sliding conditions. The results showed that a two-layer ox ide coating was formed on the alloy surface, consisting of a dense inner α-Al2O3 barrier layer and a porous outer layer predominantly composed of γ-Al2O3. The incorporation of nanoparticles contributed to coating densification, reduced porosity, and promoted a more uniform distribution of micro-arc discharges. After PEO treatment, the surface microhardness increased from 65–80 HV to approximately 245–250 HV, repre senting more than a threefold increase. The coatings also exhibited a stable tribological response, character ized by a higher yet stable coefficient of friction and improved wear resistance compared to the untreated al loy. These results demonstrate the high potential of nanomodified PEO for enhancing the operational perfor mance of aluminium–silicon alloys.