Molecular Dynamics Simulation of Oxygen Diffusion in (PuxTh1−x)O2 Crystals

Dastan D. Seitov, Kirill A. Nekrasov, D. A. Ustiuzhanin, A. S. Boyarchenkov, Yu. A. Kuznetsova, Sergey S. Pitskhelaury, Sanjeev Kumar Gupta

Data confidence 70 medium

How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

Oxygen diffusion in (PuxTh1−x)O2 mixed oxide crystals was investigated using molecular dynamics simulation. The model systems were isolated nanocrystals of 5460 and 15,960 particles, featuring a free surface. The oxygen diffusion coefficient D increased with decreasing thorium content, in accordance with the decrease in the melting temperature of (PuxTh1−x)O2 as x varied from 0 to 1. The temperature dependences D(T) exhibited non-linearity in the Arrhenius coordinates lnD = f(1/kT). The three linear segments of the plots corresponded to the superionic state, a transitional region, and the low-temperature crystalline phase. The transitional region was characterized by maximum values of the effective diffusion activation energy ED(PuO2) = 3.47 eV, ED(ThO2) = 5.24 eV and a complex collective mechanism of oxygen migration, which involved the displacement of anions into interstitial sites. At lower temperatures, an interstitialcy mechanism of oxygen diffusion was observed. The temperature dependence of D(PuO2) showed quantitative agreement with low-temperature experimental data.