Use of Processed Sugarcane Bagasse Ash in Concrete as Partial Replacement of Cement: Mechanical and Durability Properties

Shazim Ali Memon, Usman Javed, Muhammad Izhar Shah, Asad Hanif

Buildings, 2022

Full text Open access: Gold Metadata (CSL-JSON)
DOI 10.3390/buildings12101769
Data confidence 85 high
How this score is calculated

It is built from checkable properties of the record itself: whether the article has a DOI, how many independent sources confirmed its data, whether the required fields are filled in, and how recent the latest confirmation is. Disagreement between sources and a missing identifier lower it. A value of 80 or above means the record was published without further checking; 60 to 79 means it is published at reduced confidence, with a manual check advisable. A record verified by an editor by hand is never pushed below 90 by a recalculation. This scores our data about the article, not the article itself.

Abstract

Using biomass waste as supplementary cementing material (SCM) in concrete has attracted researchers’ attention for efficient waste utilization and reducing cement demand. Sugarcane bagasse ash (SCBA) is one such example of biomass waste. It is an agricultural waste obtained when sugarcane bagasse from the sugar industry is used for power generation and disposed of in open-air dumping sites. Its waste disposal causes the generation of particulate matter, degrading air quality. In this study, the effect of processed SCBA as SCM in concrete has been investigated. The processing of the SCBA involved the removal of fibrous and carbon-containing particles by sieving followed by grinding. The SCBA was ground for 45 min until the surface area was comparable to that of cement and was then used for further characterization and incorporation into concrete. The 45 min grinding time resulted in 2.92 times higher pozzolanic reactivity of the SCBA. The SCBA was incorporated by replacing cement in different weight fractions (10%, 20%, 30%, 40%) in concrete. Test results showed that the concrete workability increased with SCBA incorporation, whereas the resulting concrete density was reduced. The results of the mechanical properties, including compressive sstrength and hardened density, were enhanced upon the cement replacement by SCBA. Concrete containing 30% SCBA can be used for structural applications as its 28 days compressive strength was 21 MPa, which complies with ACI 318-16 specifications. Concrete resistance against scaling and leaching due to adverse effects of sulfuric and hydrochloric acid considerably increased with SCBA addition and was due to microstructure densification by secondary hydrates formation as lower portlandite content was detected by thermogravimetric analysis. Hence, SCBA processing increases its reactivity, as reflected by the improved mechanical properties and greater durability of SCBA-incorporated concrete.