Аннотация
This article presents the results of laboratory studies on the smelting of nickel–chromium-containing ferroalloys from low-grade nickel ores from Kazakhstan. X-ray phase analysis was performed on raw materials, which included quartz, nontronite, chromium metahydroxide, goethite, magnetite, iron chromite, and nickel (II) silicate. The reduction reactions of metal oxides with carbon and carbon monoxide were studied as the temperature increased. Experimental smelting was carried out in a Tammann furnace at 1500–1550 °C using three types of reducing agent: RK coke, as well as its mixtures with low-ash Shubarkol coal, in ratios of 75:25 and 50:50. The second option demonstrated the highest economic efficiency, achieving a 91% nickel recovery rate, reduced coke consumption, and a slag-to-metal ratio of 3.07. Chemical analysis showed that the nickel content in the obtained alloys ranged from 2.5% to 6.5%, while chromium content ranged from 2.6% to 4.5%. X-ray phase analysis confirmed the presence of Fe2Ni0.6Si, Fe5Si3, and Fe2CrSi phases in the alloy structure. Local element concentrations varied within the following ranges: Fe—55–59%, Ni—2–10%, Cr—2–7%, and Si—29–35%. The results of this study confirmed the feasibility of producing a nickel–chromium-containing alloy with a nickel content of 2–10% and a chromium content of 2–7%.