Аннотация
The article presents the results of obtaining a composite material by sintering nickel-containing raw materials mixed with carbon-containing materials, namely using coke and semi-coke. The sintering process was performed at a charge layer height of 240 mm and the temperature of the lower layer was T = 1200 °C. The results of the sieve analysis showed (a fraction of 10 mm) that the yield of a suitable composite material using coke was 68.3% and with semi-coke 67.0%. The average nickel and chromium content in the composite materials was 1.42% and 3.07%, accordingly. As a result of determining the strength characteristics of the obtained composite materials with various reducing agents by dropping from a height of 2 m onto a steel pallet, it was found that the obtained composite materials have high mechanical properties in terms of strength of 81% and 89.2%. The results of the elemental composition at the studied points and the thermal analysis of the studied composite material are presented. The mineralogical composition of the composite material is presented in the form of serpentine and nontronite, and the empty rock is made of quartz and talc. The activation energy of thermal analysis by the method of non-isothermal kinetics were calculated. The results of experiments on the production of composite materials from nickel-containing raw materials will be recommended for obtaining the optimal composition of composite materials at the stage of pilot tests and industrial development of the developed technology for processing nickel ores of the Republic of Kazakhstan. For the processing of nickel-poor nickel ores, it is of great importance to obtain optimal technological and technical and economic indicators that ensure low cost of nickel in the resulting product.