Аннотация
This paper considers the effect of aging processes on viscoelastic characteristics of vacuum residue oxidation products modified with crumb rubber. Viscoelastic properties were compared to original bitumen raw material-vacuum residue and vacuum residue oxidation products during short-term and long-term aging. The complex shear modulus of the vacuum residue and its oxidation products decreased with an increase in temperature. Short-term aging resulted in increased shear modulus for all samples.The vacuum residue oxidation product modified with crumb rubber had the maximum values of the rutting parameter and fatigue parameter. There was an expansion of the temperature range of plasticity: for the vacuum residue oxidation product with crumb rubber, its value was 67.2 °C. The curves of the black diagram of the modified vacuum residue oxidation product are shifted towards smaller phase angles with the increase in the shear modulus, which indicates the increase in the stiffness and elasticity of the rubber bitumen binders. The vacuum residue oxidation product modified with crumb rubber corresponded to the rubber bitumen binder of the grade RBB 60/90, according to its physical and mechanical indicators.