Аннотация
Along with the growth in the production of metallurgical grade silicon and high-silicon ferrous alloys, there is a significant increase in the formation of microsilica, which is an ultra-fine technogenic waste. The direct application of microsilica in ore-thermal furnaces is hindered by low bulk density, poor gas permeability, and high dusting. This paper explores the thermophysical and microstructure properties of briquettes based on microsilica, which includes various types of carbonaceous reducing agents such as semi-coke and coal. For manufacturing, the liquid glass was used as the inorganic binder for the preparation of microsilica briquettes. The best variants were chosen based on strength tests carried out during preliminary studies. In the laboratory tests, the stability of the briquettes at elevated temperatures was evaluated. Samples were heated to 1000–1500 °C and subjected to impact testing. Scanning Electron Microscopy with Energy Dispersive Spectroscopy (SEM/EDS) was used to investigate the microstructure and local elemental distribution. It was revealed that the calcinated briquettes of the microsilica–semi-coke mixture have better thermal stability compared to the samples with coal and withstand the temperature range up to 1500 °C. The microstructure of the briquette from the microsilica-semi-coke mixture is characterized by the formation of a more uniform silicate matrix with the presence of a homogeneously distributed carbonaceous component. Coal-based samples show higher heterogeneity and porosity. Therefore, it can be stated that the selection of carbonaceous reductants is one of the key factors influencing the thermal stability of microsilica briquettes.