Аннотация
This study assessed whether electrochemical activation of mixing water can enhance autoclaved aerated concrete (AAC), in which fly ash replaces sand as the siliceous component. Mixing water was electrolyzed in a diaphragm-type “Melesta” unit to obtain the catholyte and anolyte, and fly ash was pre-exposed to the catholyte for up to 15 min. The material’s behavior was evaluated using slurry flow tests, scanning electron microscopy, Fourier-transform infrared spectroscopy, macropore-uniformity analysis, mercury intrusion porosimetry, and shrinkage and short-term durability indicators. At an approximately constant density class near 600 kg/m3, the catholyte-pretreated fly-ash AAC mixes showed a near-monotonic increase in compressive strength with increasing fly-ash replacement (relative to the sand-based reference), while fresh-mixture fluidity decreased. The pore structure became more uniform, as indicated by a decrease in the standard deviation of pore diameters from 0.175 to 0.133 mm, and porosimetry indicated a higher micro-porosity fraction in fly-ash AAC than in sand-based AAC. Capillary shrinkage remained essentially unchanged, and short-term durability indicators (durability coefficients after 25 cycles) showed a small improvement. Overall, electrochemically activated water promoted a more regular pore system and stronger interpore walls under autoclave curing, supporting higher fly-ash utilization without loss of dimensional stability. The results are limited to one fly-ash source (Ekibastuz TPP); transferability should be verified using ashes with different glass content, fineness, and carbon/LOI.