Аннотация
This paper presents the results of a metallographic and tribological study of 86WC-10Co-4Cr coatings obtained by the HVOF method on the Termika-3 unit at varying spraying distances. The influence of spraying distance on the coating microstructure, phase composition, as well as mechanical and tribological properties, was studied. The phase composition, microstructure and elemental distribution were analyzed using X-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy techniques. The hardness was measured on a Vickers microhardness tester, the friction coefficient and wear rate were investigated using a tribometer. According to the results of the study, it was found that the optimum spraying distance for 86WC-10Co-4Cr coatings with improved wear resistance and hardness characteristics and low porosity is 300 mm.