Аннотация
Research analysis reveals factors influencing third-phase crud formation and composition during metal extraction, including solution composition, solid suspensions, organic compounds, colloidal compounds (e.g., silicic acid), and extractant purity. Compositional analysis of copper-containing sulfuric acid solutions (1.25 g/dm3 copper) identifies principal sulfate-forming components. Copper extraction was studied using extractants LIX 984N, ACORGA M5774, and M5640 at different ratios of the organic phase to the aqueous O:A (from 1:2 to 1:10). Suppressive impact of 10 vol.% CR60 additive on third-phase crud formation during copper extraction with LIX 984N, ACORGA M5774, and M5640 is analyzed, with ACORGA M5774 being the most effective. Physicochemical analysis characterizes CR60’s active substance as poly(sodium 4-styrenesulfonate) with steel-suppression properties, and its structural formula is determined. Optimal copper extraction conditions establish ACORGA M5640’s 24% efficiency, followed by ACORGA M5774 at 15%. CR60 reduces crud formation, with 5 cm3 of ACORGA CR60 added to sulfuric acid solution reducing interfacial crud formation by 2–3 times. Optimal extraction parameters include 1:2 O:A ratio, 20 ± 5 °C temperature, 5 cm3 CR60 additive, 5 min process duration, and 1-day settling time. ACORGA M5774 (10 vol.% in kerosene) is recommended as an extractant, with 2–3 stages of countercurrent extraction.