Аннотация
Copolymers were obtained in this work and the methodology for their synthesis was worked out. Various fillers were selected for the polymer coating. Resulting copolymers have good adhesion required for composite protective coatings. An experiment was conducted to determine the corrosion resistance of metals coated with copolymers when exposed to aggressive environments, as well as to determine the hardness and thickness of the polymer coatings obtained. It was found that the polymer coating filled with bronze powder, despite the small thickness of 43.4 μm, hasthe best adhesion and corrosion properties, as well as having the highest hardness values of 80.5 HB. Such physical and mechanical properties of polymer coatings allow them to be used as protective coatings for metal products working under the influence of aggressive media.