Аннотация
The research shows the results of electrolyte-plasma treatment influence on structure-phase state, mechanical properties and wear-resistance of drilling tool steel samples. The comparative analysis of microstructure, microhardness and wear-resistance of the samples in initial state and after electrolyte-plasma treatment is represented. It was found out that 18CrNi3MoA-Sh steel microstructure has fine-grained martensite-bainite structure after the treatment. It was determined that 18CrNi3MoA-Sh steel possesses high wear-resistance after electrolyte-plasma treatment, so that technology is characterized by low power consumption and cost price. The initial state microhardness is 2800 MPa on the average. Microhardness on the bearing lane surface after electrolyte-plasma processing is 7500 MPa on the average. Microhardness increases in 2-2.5 times more before treatment that indicates the technology efficiency.