Аннотация
This study examined the effect of partially replacing semi-reinforcing carbon black grade N550 (up to 10 pts. wt.) and fully replacing industrial chalk with natural shungite mineral in industrial formulations of elastomer compositions intended for manufacturing various rubber technical products. It has been shown that due to the high content of carbon and silicon components in the composition of shungite mineral micropowders, their use as a filler in elastomer formulations significantly improves the physical and mechanical properties of rubber technical products (RTPs) manufactured using such compositions. It was determined that the use of SM as a partial replacement for carbon black in rubbers intended for molded rubber technical products contributes to a reduction in Mooney viscosity (up to 26.8%) and optimal vulcanization time (up to 23.7%), achieving rubbers with the required set of physical-mechanical properties and with an enhancing sealing capability (up to 19.7%). It has been established that the use of shungite mineral micropowders as a complete replacement for industrial chalk increases the strength of rubber products (RTPs) by up to 18.5% and enhances their resistance to liquid aggressive environments.