This work is devoted to the study of the possibility of recycling bar scrap of stainless metals using radial-shear rolling. In the course of studies on the deformation of bar scrap in the form of pins made of 12X18N9T stainless austenitic steel on a radial-shear rolling mill, the resulting bar was obtained microstructure of two different types: on the periphery an equiaxed ultrafine-grained structure with a grain size of 0.4–0.6 microns was formed; in the axial zone anoriented, banded texture was obtained. This discrepancy in the structure of the peripheral and axial zones, together with the results of cross-section microhardness measurements of samples made of 12X18N9T austenitic stainless steel with a total degree of deformation of 44.4 %, indicates the gradient nature of the resulting microstructure.