Аннотация
A composite based on humic acid (HA) and reduced graphene oxide (rGO) was synthesized to evaluate the effect of rGO on the structural, functional, thermal, and preliminary phenol adsorption properties of humic acid. The incorporation of rGO increased the carbon content from 47.34 to 55.61 wt.% and decreased the oxygen content from 48.31 to 40.79 wt.%. At the same time, the total content of carboxyl and phenolic hydroxyl groups increased from 5.00 to 5.47 mmol/g, indicating improved accessibility of oxygen-containing functional sites. FTIR spectroscopy confirmed the retention of the main functional groups of the initial components after composite formation. Thermogravimetric analysis showed enhanced thermal stability, with the residual mass at 1000 °C increasing from 59.21 to 70.03%. Electron microscopy revealed the formation of a developed wrinkled surface morphology. Preliminary phenol adsorption experiments showed that the HA-rGO composite exhibited higher adsorption capacity than the initial HA and rGO. This improvement was attributed to the combined contribution of oxygen-containing functional groups and the aromatic carbon structure of rGO, which may promote hydrogen bonding and π-π interactions with phenol molecules.