Аннотация
ZnS is one of the most promising wide-bandgap semiconductors for optoelectronic and sensing applications owing to its efficient ultraviolet–blue emission, high exciton binding energy, and chemical stability. However, the synthesis of ZnS nanocrystals in silicon-compatible porous matrices remains largely unexplored. In this work, ordered arrays of ZnS nanocrystals were synthesized for the first time in SiO2/Si track templates fabricated by swift heavy ion irradiation followed by selective chemical etching. ZnS nanocrystals were deposited by electrochemical deposition from aqueous solutions containing ZnCl2 and thiourea precursors. The structural, optical, and electrical properties of the resulting ZnS/SiO2/Si nanocomposites were investigated using scanning electron microscopy, X-ray diffraction, Raman spectroscopy, photoluminescence spectroscopy, and electrical measurements. The fabricated templates contained vertically aligned pores with a density of approximately 108 cm−2 and an average diameter of about 500 nm. Electrochemical deposition resulted in a pore filling efficiency of approximately 88%. X-ray diffraction analysis confirmed the formation of crystalline ZnS with a cubic zinc blende structure. The nanocomposites exhibit intense ultraviolet–blue photoluminescence in the 335–477 nm range, with pronounced emission peaks at 372 and 400 nm characteristic of ZnS nanocrystals. Current–voltage measurements indicate predominantly electronic conductivity, with a conductivity of 1.54 × 10−6 Ohm−1·cm−1, comparable to values reported for polycrystalline ZnS films. To support the experimental observations, the electronic structure of ZnS was analyzed using density functional theory within the LCAO framework. The calculated bandgap of 3.4 eV is consistent with previously reported theoretical and experimental data. The obtained results demonstrate that SiO2/Si track templates provide a promising platform for the fabrication of ordered ZnS nanoarrays with potential applications in silicon-compatible optoelectronic and sensing devices.