Methods for the preparation of aluminum hydroxides and alumina-supported catalysts through the interaction of activated Al–In–Ga alloys with water were developed. Bayerite was obtained from an alloy containing 99.0% Al + 0.5% In + 0.5% Ga at 303 K, while pseudoboehmite was synthesized from 90% Al + 5% In + 5% Ga at 363 K. The maximum specific surface area of aluminum oxide reached 700 m2/g. Dehydration of aluminum hydroxides proceeds via a sigmoidal mechanism with induction, acceleration, and deceleration stages. The dehydration rate increases with calcination temperature. Kinetic analysis revealed both kinetic and diffusion-controlled transformation regions for pseudoboehmite and bayerite. Transformation of pseudoboehmite into γ-Al2O3 at 523–673 K preserves a high specific surface area of 630–640 m2/g. Two platinum deposition methods were proposed: synthesis in the presence of soluble platinum salts and incorporation of Pt into the Al–Ga–In alloy followed by reaction with water. Alongside metallic Pt, Ptδ+, Pt2+, and Pt4+ species were detected and reduced to Pt0 at 900 K. Alumina–platinum catalysts showed high activity in cyclohexane dehydrogenation. A Zn–Al catalyst for methanol decomposition was developed, providing up to 70% H2 in gaseous fuel and complete methanol conversion at 573 K.