Аннотация
This study investigated the production of spodumene concentrate and lithium carbonate from a low-grade pegmatite ore containing approximately 0.26 wt.% Li2O. The ore consisted predominantly of a quartz–feldspar aluminosilicate matrix with dispersed spodumene mineralization, which complicates conventional processing approaches. Preliminary lithium concentration was performed by dense media separation (DMS) using an industrially applicable ferrosilicon-based suspension. The highest separation efficiency was achieved for the −4.0/+2.8 mm fraction, producing a DMS concentrate containing 5.77 wt.% Li2O with 98% lithium recovery. The obtained spodumene concentrate was subjected to decrepitation at 1000–1100 °C to convert α-spodumene into the more reactive β-modification, followed by sulfation roasting with concentrated sulfuric acid at 250–270 °C. The productive leach solution obtained after water leaching contained up to 12.1 g/L Li2O. After purification from iron-bearing impurities and precipitation with sodium carbonate, a lithium carbonate product containing at least 98.8 wt.% Li2CO3 was obtained. Approximately 53% of the lithium contained in the original ore was recovered into the DMS feed fraction, whereas the overall lithium recovery into lithium carbonate reached about 45% relative to the ore and approximately 70% relative to the concentrate.