Аннотация
nanocomposites. The materials were fully characterized and the results showed that both materials were decorated with nanoparticles of size of 5-25 nm. The natural and modified zeolites were used for the removal of iodide from aqueous solutions of initial concentration of 30-1400 ppm. Natural zeolite showed no affinity for iodide while silver forms were very efficient reaching a capacity of up to 132 mg/g. Post-adsorption characterizations showed that AgI was formed on the surface of the modified zeolites and the amount of iodide removed was higher than expected based on the silver content. A combination of experimental data and characterizations indicate that the excess iodide is most probably related to negatively charged AgI colloids and Ag-I complexes forming in the solution as well as on the surface of the modified zeolites.