Introduction The article presents the results of chemical and physicochemical analysis of initial lithium-containing hydromineral raw materials and sorbent based on bentonite clay with titanium oxide addition. Methods It is established that the mineral is montmorillonite group and kaolinite according to the results of the analysis of the microstructure and elemental composition of bentonitic clay of the Darbazinsky deposit. Brine is characterized by the change of lithium chloride content in the range of 403-1001 mg/l. Physical and mechanical characteristics of the obtained sorbents based on bentonite clay and titanium oxide additive are characterized by a high mechanical strength of 5.31 MPa, density of up to 2,6 g/cm3, and specific surface area of 1572 cm2/g. The technological parameters of sorption extraction of lithium chloride from lithium-containing hydromineral raw materials were optimized using the system analysis “STATISTICA” developed by StatSoft company. It is established that to increase the rate of lithium chloride extraction from brine, it is necessary to maintain the rate of brine flow within 8 l/min at maximum humidity of solution output up to 43g/m3 on the basis of the obtained volumetric graphical dependencies. Results The microstructure of the used sorbents with titanium oxide addition up to 20% is characterized by the predominance of lithium chlorides, which are represented by heap-shaped, prismatic crystals. Conclusion The maximum amount of lithium chloride in the form of clusters of light-white crystals of tabular shape on the surface of the sorbent is observed at increasing the content of titanium oxide up to 40%.