Аңдатпа
Zincate-manganites with the composition NdM2IIZnMnO6 (MII− Mg, Ca) were synthesized using ceramic technology from oxides of Nd (III), Zn (II), Mn (III) and carbonates of alkaline-earth metals - magnesium and calcium. X-ray patterns of the prepared substancies were measured on a DRON-2.0 diffractometer. We established that they crystallize in the cubic system with the following unit cell parameters: NdMg2ZnMnO6 – а=13.927±0.035 Å, Z = 4, V0 = 2701.36±0.11 Å3, V0el.cell. = 675.34±0.03 Å3, ρX-ray = 4.20, ρpycn. = 4.19±0.01 g/cm3; NdCa2ZnMnO6 – а=13.910±0.030 Å, Z = 4, V0 = 2691.45±0.10 Å3, V0el.cell. = 672.86±0.03 Å3, ρX-ray = 4.04, ρpycn. = 4.01±0.08 g/сm3. The temperature dependence of the heat capacity of NdMg2ZnMnO6 and NdCa2ZnMnO6 was studied by dynamic calorimetry in the range of 298.15-673 K on the IT-S-400 calorimeter. Five parallel experiments were performed at each temperature point with 25 K step. The results were averaged and analyzed using mathematical statistics. As a result of calorimetric studies of the heat capacity, within the temperature range of 298.15-673 K, we discovered on the curves of the temperature dependence of heat capacity the phase transitions of the II kind at the following temperatures: 373, 548 К- NdMg2ZnMnO6, 448, 573 К – NdCa2ZnMnO6. These phase transitions were probably due to Schottky effects -the transition from semiconductivity to metallic conductivity, and variations in capacity, dielectric permittivity, the occurrence of Curie or Neel points. The equations of the temperature dependence of the heat capacity were derived on the basis of the experimental values with account the temperatures of the phase transitions. By the ion increment method, we calculated the standard entropies of the compounds investigated. We calculated the temperature dependences of С°р(Т) and thermodynamic functions Н°(Т)-Н°(298.15), S°(T) and Фхх(Т).Forcitation:Kasenov B.K., Kasenova Sh.B., Sagintaeva Zh.I., Kuanyshbekov Е.Е., Turtubaeva М.О. Synthesis and study of thermodynamic properties of new zincate-manganites NdM2IIZnMnO6 (MII − Mg, Ca). Izv. Vyssh. Uchebn. Zaved. Khim. Khim. Tekhnol. 2018. V. 61. N 3. P. 16-20