Аңдатпа
It was demonstrated that various defects can be induced in halide crystals by irradiation with swift heavy ions. Here, we irradiated barium fluoride (BaF2) single crystals with 220 MeV xenon ions at room temperature and performed stepwise thermal annealing up to the temperature of 825 K to study the kinetics of ion-induced defects at different temperatures. Optical spectroscopy was utilized for the measurement of the wide range of absorption spectra from NIR to VUV. A sharp decrease in the F2 absorption peak was observed for the samples annealed in the temperature range of 400–450 K. This result can be explained by their recombination with anion interstitials during thermal decay of the complex hole centers. The mobile interstitials, those did not recombine with the F2 centers, increase the absorption peaks in the 9–10 eV region, which can be associated with interstitial aggregates.