Аңдатпа
This paper presents the first results on formation and study of structure and properties of micro-and nanocomposite combined coatings.By means of modeling the deposition processes (deposition conditions, current density-discharge, plasma composition and density, voltage) we formed the three-layer nanocomposite coatings of Ti-Al-N/Ti-N/Al 2 O 3 .The coating composition, structure and properties were studied using physical and nuclear-physical methods.The Rutherford proton and helium ion backscattering, scanning electron microscopy with microanalysis, grazing incidence X-ray diffraction, as well as nanohardness tests (hardness) were used.Measurements of wear resistance and corrosion resistance in NaCl, HCl and H 2 SO 4 solutions were also performed.For testing mechanical properties such characteristics of layered structures as hardness H, elastic modulus E: H 3 /E 2 etc. were measured.It is demonstrated that the formed three-layer nanocomposite coatings have hardness of 32 to 36 GPa and elastic modulus of 328 ± 18 to 364 ± 14 GPa.Its wear resistance (cylinder-surface friction) increased by factor of 17 to 25 in comparison with the substrate (stainless steel).The layers thickness was in the range of 56-120 µm.