Аңдатпа
Abstract Polycrystalline nickel nanotubes with diameter of 380 nm and wall thickness 95 nm were synthesized by electrochemical method using PET track-etched membranes with thickness of 12 μm. A comprehensive study of the structural, morphological and electrical characteristics of Ni nanotubes irradiated with C+13 ions with energy 1.75 MeV/nucleon and fluence ranging from 109 to 5 × 1011 cm-2 was carried out. The ability of modification of structural parameters such as lattice parameter and the average size of crystallites and conductivity of Ni nanotubes by irradiation was shown.