This study investigates the agglomeration of chromium-containing dust from ferroalloy production using rigid vacuum extrusion. Direct utilization of fine technogenic materials in submerged arc furnaces is limited due to poor gas permeability, increased dust generation, and unstable smelting conditions. The aim of this work was to compare bentonite and polymer binders in brex production and evaluate their metallurgical applicability. Chromium-containing dust from the gas-cleaning system of the Aktobe Ferroalloy Plant (TNC Kazchrome JSC, ERG) was characterized using chemical analysis and SEM/EDS methods. The material exhibited a heterogeneous structure composed mainly of chromium-containing spinel, silicate, and oxide phases. Pilot-industrial extrusion tests were performed using J.C. Steele & Sons equipment with bentonite (10 wt.%) and polymer binder TD 021.005.BS (2.5 wt.%). The polymer binder provided improved brex geometry and significantly higher mechanical strength, achieving impact strength values up to 89.5% after curing. SEM/EDS analysis of the obtained brexes confirmed the formation of a dense agglomerated structure with uniform distribution of chromium-containing phases. Thermodynamic modeling using FactSage 8.4 showed that brex addition does not significantly affect slag composition, phase equilibria, or metal quality during high-carbon ferrochrome smelting. The results demonstrate the feasibility of polymer binders for efficient recycling of chromium-containing technogenic wastes by rigid vacuum extrusion.