Despite major advances in polymer composites for Fused Filament Fabrication (FFF), designing environmentally sustainable materials from bio-based resources remains a key research priority. The objective of this study is to check the processability and properties of sustainable PETG/cork composites processed via FFF technology. Filaments with 5 and 10% of cork were created using a twin-screw extruder. Samples from these filaments were printed by FFF technology, and subsequently subjected to morphological, thermal and mechanical testing. As a result of the study, it was proved that the 3D-printing process did not result in a tensile strength decrease with an increasing cork percentage, as observed in mechanical testing of the filament. The addition of cork significantly increased plasticity without decreasing tensile strength when introducing 10% of cork particles. The interfacial temperatures of the prepared composites did not differ much from the polymer matrix and were 79.55 °C, 77.56 °C, 76.67 °C for PET-G, PET-G + 5% cork, and PET-G + 10% cork, respectively. Thermal conductivity decreased significantly as the percentage of cork increased. This work shows that FFF technology is one of the most suitable manufacturing options for PETG + 10% cork composites to produce things with low conductivity and the same thermal and mechanical properties as pure PETG.