Аңдатпа
The modification of road bitumen using micro-sized carbonaceous materials offers a promising route to enhance pavement performance; however, the influence of microdispersed coke derived from coal and petroleum sources has not been sufficiently clarified. In this study, coal and petroleum coke from Pavlodar Petrochemical Plant LLC (Pavlodar, Kazakhstan) were mechanochemically activated and used as the modifiers for BND 100/130 bitumen, produced by Asphaltbeton 1 LLC (Almaty, Kazakhstan). X-ray diffraction and scanning electron microscopy were used to determine the structure and morphology of the resulting coke powders. Standard tests and the Superpave Multiple Stress Creep and Recovery (MSCR) methodology were used to determine the physico-mechanical and rheological properties of the modified binders. Microdispersed granular coke powders produced after mechanochemical activation had a minimum average particle diameter of 8.28 µm (petroleum coke) and 16.64 µm (coal coke), and were mainly an amorphous carbon phase with traces of graphite. Addition of 1 wt.% microdispersed coke resulted in better performance of binder and an enhancement in grades of BND 100/130 to BND 70/100, in line with ST RK 1373-2013. MSCR testing showed that Jnr3.2 is between 2.0–3.0 kPa−1, which is in the S category of AASHTO M 332-20. This study showed how micro-sized coal and petroleum coke can be effectively used as a high-carbon modifier in bitumen, which reflects the possibility of their practical use in asphalt pavements that are subjected to normal traffic conditions.