Аңдатпа
This study investigates the influence of preliminary severe plastic deformation on the efficiency of ion-plasma nitriding (IPN) and the formation of a nitrided layer in 12Kh18N10T austenitic stainless steel. Two types of surface mechanical treatment were compared: vibro-impact ball mechanical treatment (VIMT) and ultrasonic nanocrystalline surface modification (UNSM). After the preliminary treatments, the samples were subjected to ion-plasma nitriding at 500 °C for 10 h using ammonia (NH3) as the working gas. The phase composition, microstructure, elemental distribution, surface roughness, microhardness, and scratch resistance were analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDS) analysis, profilometry, instrumented indentation, and progressive scratch testing. The results show that both types of preliminary treatment promote the formation of a nitrogen-enriched diffusion layer. The UNSM-treated samples exhibited more pronounced peak broadening and shifting in XRD patterns, indicating a higher level of lattice distortion and nitrogen supersaturation. The maximum nitrogen concentration in the near-surface region reached 15.56 wt.%. Microhardness increased significantly after nitriding for both treatments. Under the selected processing conditions, the UNSM + IPN samples demonstrated a thicker diffusion layer, lower surface roughness, and higher critical loads in scratch testing, indicating improved resistance to surface damage compared with VIMT + IPN samples. The obtained results highlight the important role of the defect structure formed during preliminary treatment in controlling nitrogen diffusion and the resulting mechanical and tribological properties of ion-plasma nitrided austenitic stainless steel.